Threading-dislocation-free nanoheteroepitaxy of Ge on Si using self-directed touch-down of Ge through a thin SiO2 layer

ABSTRACT

A method of forming a virtually defect free lattice mismatched nanoheteroepitaxial layer is disclosed. The method includes forming an interface layer on a portion of a substrate. A plurality of seed pads are then formed by self-directed touchdown by exposing the interface layer to a material comprising a semiconductor material. The plurality of seed pads, having an average width of about 1 nm to 10 nm, are interspersed within the interface layer and contact the substrate. An epitaxial layer is then formed by lateral growth of the seed pads over the interface layer.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority to U.S. Provisional Patent Application Ser. No. 60/501,274 filed on Sep. 9, 2003, the disclosure of which is incorporated herein by reference.

GOVERNMENT RIGHTS

This invention was made with government support under Award No. DMR-0094145 awarded by the National Science Foundation. The government has certain rights in the invention.

FIELD OF THE INVENTION

The present invention relates to. semiconductor devices and methods for their manufacture and, more particularly, relates to epitaxial growth of lattice mismatched systems.

BACKGROUND OF THE INVENTION

Conventional semiconductor device fabrication is generally based on growth of lattice-matched layers. A lattice mismatched epitaxial layer at a semiconductor interface can lead to a high density of dislocations that degrade semiconductor device performance. Over the past several years, however, there has been increased interest in epitaxial growth of lattice-mismatched semiconducting material systems. Lattice mismatched systems can provide a greater range of materials characteristics than silicon. For example, the mechanical stress in a lattice mismatched layer and control of its crystal symmetry can be used to modify the energy-band structure to optimize performance of optoelectronic devices. Lattice mismatched systems can also enable compound semiconductor devices to be integrated directly with Si-based complementary metal oxide semiconductor (CMOS) devices. This capability to form multifunction chips will be important to the development of future optical and electronic devices.

Problems arise, however, because an epitaxial layer of a lattice-mismatched material on a substrate is often limited to a critical thickness (h_(c)), before misfit dislocations begin to form in the expitaxial material. For example, h_(c)=2 nm for a germanium epitaxial layer on a silicon substrate. Because of the relatively small h_(c) and the large dislocation densities at thicknesses greater than h_(c), use of the heteroepitaxial layer is impractical.

Thus, there is a need to overcome these and other problems of the prior art and to provide a method to grow defect free heteroepitaxial layers of lattice mismatched systems.

SUMMARY OF THE INVENTION

According to various embodiments, the present teachings include a method of forming a semiconductor layer including forming an interface layer on a portion of a substrate. The interface layer is exposed to a material comprising a semiconductor material to form a plurality of seed pads interspersed within the interface layer and contacting the substrate. A semiconductor layer is then formed by lateral growth of the seed pads over the interface layer.

According to various embodiments, the present teachings also include a method of forming a semiconductor layer including forming an oxide layer on a portion of a semiconductor substrate. A plurality of seed pads comprising germanium are formed by self-directed touchdown. The plurality of seed pads are interspersed within the oxide layer and contact the semiconductor substrate. A germanium layer is then formed by lateral growth of the seed pads over the oxide layer.

According to various embodiments, the present teachings further include a semiconductor device including a substrate and an oxide layer disposed on a portion of the substrate. The semiconductor device also includes a plurality of seed pads formed by self-directed touchdown. The plurality of seed pads are separated from each other by the oxide layer. The semiconductor device further includes a semiconductor layer disposed over the substrate, wherein the semiconductor layer is formed by lateral growth of the seed pads over the oxide layer.

It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention, as claimed.

The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate several embodiments of the invention and together with the description, serve to explain the principles of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 depicts a cross-section of a substrate in accordance with exemplary embodiments of the invention.

FIG. 2 depicts a cross-sectional view of an interface layer on a substrate in accordance with exemplary embodiments of the invention.

FIG. 3A depicts a cross-sectional view of seed pad sites interspersed in an interface layer in accordance with exemplary embodiments of the invention.

FIG. 3B depicts a top-down view of seed pad sites interspersed in an interface layer in accordance with exemplary embodiments of the invention.

FIG. 4A depicts a cross-sectional view of seed pads on a substrate and separated by portions of the interface layer in accordance with exemplary embodiments of the invention.

FIG. 4B depicts a top-down view of seed pads on a substrate and separated by portions of the interface layer in accordance with exemplary embodiments of the invention.

FIG. 5 depicts a cross-sectional view of a semiconductor layer formed by lateral growth of seed pads over portions of the interface layer in accordance with exemplary embodiments of the invention.

FIG. 6 depicts a cross-sectional view of a second semiconductor layer on the semiconductor layer in accordance with exemplary embodiments of the invention.

DESCRIPTION OF THE EMBODIMENTS

In the following description, reference is made to the accompanying drawings that form a part thereof, and in which is shown by way of illustration specific exemplary embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention and it is to be understood that other embodiments may be utilized and that changes may be made without departing from the scope of the invention. The following description is, therefore, not to be taken in a limited sense.

As used herein, the term “self-directed touchdown” refers to a nucleation and growth process that is initiated without reliance on an photolithographic mask to pattern a substrate or other layer.

As used herein, the term “nanoheteroepitaxy” refers to engineering a heterojunction at the nanoscale to relieve lattice strain.

FIGS. 1 to 6 depict exemplary semiconductor devices with nanoheteroepitaxal layers and manufacturing methods to form semiconductor devices with nanoheteroepitaxal layers having a lattice mismatched substrate and semiconductor layer in accordance with various embodiments of the invention. The semiconductor devices comprise a plurality of seed pads formed by self-directed touch-down through a portion of an interface layer and on a substrate. A semiconductor layer can then be formed by coalescence of the seed pads over the portions of the interface layer. The semiconductor layers formed by the exemplary methods have a sufficiently low threading-dislocation density, regardless of the critical thickness of the semiconductor layer, so that the deposited semiconductor layer can be effectively used for integrated circuit applications. For ease of illustration, the invention will be described with reference to a manufacturing process for formation of an epitaxial layer of germanium (Ge), having a lattice parameter of about 5.66 Å, on silicon (Si), having a lattice parameter of about 5.44 Å.

Referring to FIG. 1, a substrate 10 is shown. Substrate 10 can be, for example, a silicon substrate. Other substrate materials can include any semiconductor material having a lattice-mismatch to a desired epitaxial layer. The terms “lattice-mismatch” and “lattice-mismatched material” as used herein refer to any materials whose lattice parameters in a given crystalline plane or direction are not identical. Lattice-mismatched materials can include, but are not limited to, silicon and germanium, silicon and carbon, silicon and GaAs, silicon and InP, and silicon and gallium nitride.

As shown in FIG. 2, an interface layer 20 can be formed on substrate 10. Interface layer 20 can be, for example, an oxide layer, such as, a SiO₂ layer, having a thickness of about 1 Å to about 30 Å. The SiO₂ layer can be formed by methods known in the art, such as, treating substrate 10 in a Piranha solution or by thermal growth. Other interface materials can include, but are not limited to, silicon nitride, siliconoxynitride, anodized aluminum oxide (AAO), and other oxides. In various embodiments, interface layer 20 can comprise an amorphous material.

In various embodiments, properties of interface layer 20, such as surface roughness and thickness, can be controlled to tailor the defect morphology of the epitaxial layer. For example, interface layer 20 can be formed using H₂O₂ to achieve a monolayer of atomically flat SiO₂ on a hydrogenated Si(100) substrate.

After forming interface layer 20 on substrate 10, interface layer 20 can be exposed to a material comprising a semiconductor material. Exposure temperatures can be about 500° C. to about 750° C. The semiconductor material can comprise, for example, Ge. In various embodiments, molecular beam epitaxy can be used to expose interface layer 20 to Ge. As shown in FIGS. 3A and 3B, the Ge can react with interface layer 20, to form interface layer free areas 30, exposing portions of substrate 10. Interface layer free areas 30 can form, for example, through reaction of the Ge with the oxide film as follows: SiO2(s)+Ge(ad)→SiO(g)+GeO(g). Interface layer free areas 30 can be randomly distributed to form a remaining portion of interface layer 25, and can be about 2 nm to about 8 nm wide. The spacing between interface layer free areas can be about 2 nm to about 14 nm.

As exposure to Ge by molecular beam epitaxy continues, Ge can deposit in interface layer free areas 30. There is generally no deposition on remaining portions of interface layer 25, due to selective deposition. This self-directed touch-down of Ge on Si occurs without lithography to pattern the substrate or interface layer. The regions of Ge growth on Si substrate 10 can form crystalline Ge islands, referred to herein as seed pads 40, shown in FIGS. 4A and 4B. Seed pads 40 can then laterally overgrow and coalesce, as exposure to Ge continues. As lateral growth of Ge seed pads 40 over remaining SiO₂ oxide layer 25 continues, Ge seed pads 40 coalesce into a single semiconductor layer. The semiconductor layer can be a virtually defect free single crystalline epitaxial lateral overgrowth (ELO) layer.

FIG. 5 shows a semiconductor layer 50 formed by coalesced seed pads having an atomically abrupt interface with substrate 10. Semiconductor layer 50 can be virtually defect-free having a threading dislocation density of about 1×10⁵ cm⁻² or less. Stacking faults can exist over the remaining oxide layer patches 25, but generally terminate within about 80 nm from the SiO₂-Ge interface. The thickness of semiconductor layer 50 can be greater than the critical thickness h_(c), for example, greater than the critical thickness of 2 nm for 100% Ge on Si. Seed pads 40 can have an average width of about 1 nm to 10 nm. The distance between seed pads can be about 3 nm or more.

In various embodiments, a second semiconductor layer 60 can be deposited over the semiconductor layer. The second semiconductor layer can comprise one or more materials from Group II, Group III, Group IV, Group V, and Group VI, such as, for example, GaN, GaAs, AlGaAs, InGaP, AlInP, AlInGaP, InGaAsN, SiGe. As shown in FIG. 6, second semiconductor layer 60 can be formed on semiconductor layer 50.

A specific example of nanoheteroepitaxy to grow virtually dislocation-free lattice mismatched materials will now be provided. It is to be understood that the disclosed examples are exemplary and in no way are intended to limit the scope of the invention.

EXAMPLE 1

Samples I was undoped Si(100) including an interface layer of SiO₂. Sample II was undoped Si(100) stripped of an interface layer by exposure to HF.

Both sample substrates were first treated to remove contaminates by immersion in a Piranha solution for about 5 minutes to form a thin layer of SiO₂ on the substrate. The Piranha solution was prepared by mixing 4 volumetric parts of 2M H₂SO₄ with 1 volumetric part of 30 wt % H₂O₂. The samples were then treated for 5 minutes in an HF solution to remove the SiO₂ layer. The HF solution was prepared by diluting a 49 wt % electronics grade HF solution to 11 wt % by deionized H₂O. The Piranha-HF treatments were repeated three times.

A fresh Piranha solution was prepared and Sample I was treated at 80° for 10 minutes to form a thin layer of chemical oxide. After treatment, Sample I was rinsed with deionized H₂O, and blow-dried with N₂. No chemical oxide layer was formed on Sample II.

Sample I was then immediately loaded into an ultrahigh vacuum molecular beam epitaxy (UHV-MBE) chamber having a base pressure of 4×10⁻¹⁰ Torr. Sample II was immediately loaded into the UHV-MBE chamber after the third HF treatment that removed the oxide layer. Both of the samples were heated to 620° C. and a Knudsen effusion cell was used to expose the samples to Ge. The effusion cell was operated at 1200° C. for a Ge growth rate of 100 nm/hour. During growth of Ge, the chamber pressure was below 1×10⁻⁹ Torr.

Cross sectional transmission electron microscopy (XTEM) showed that, in Sample I, amorphous oxide regions were interspersed with Ge seed pads. A single crystalline Ge ELO layer, approximately 4 μm thick, covered the amorphous oxide regions and seed pads. The thickness of the oxide layer regions in Sample I was determined to be 1.2 nm. The average dimension of the seed pads was about 7 nm, and the spacing between the seed pads ranged from 4 nm to 12 nm.

XTEM further showed that the Ge layer of Sample II, having no seed pads, contained a network of dislocation segments primarily within 250 nm from the Ge-Si interface. In contrast, the Ge ELO layer of Sample I was free of a dislocation network. Only stacking faults emanating from the seed pad-Ge interface existed along the {111} planes in the Ge ELO layer of Sample I. Those stacking faults terminated within 80 nm of the interface. As a result, Sample I, fabricated with the oxide layer that resulted in seed pads, formed an atomically abrupt Ge-Si interface and a virtually defect free Ge ELO layer. Sample I had a threading dislocation density of about 1×10⁵ cm⁻² or less. Sample II, however, formed without the oxide layer and seed pads, formed a Ge layer containing a network of dislocation segments.

Other embodiments of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. It is intended that the specification and examples be considered as exemplary only, with a true scope and spirit of the invention being indicated by the following claims. 

1. A method of forming a semiconductor layer comprising: forming an interface layer on a portion of a substrate; exposing the interface layer to a material comprising a semiconductor material to form a plurality of seed pads interspersed within the interface layer and contacting the substrate; and forming a semiconductor layer by lateral growth of the seed pads over the interface layer.
 2. The method of forming a semiconductor layer of claim 1, wherein exposing the interface layer to a material comprising a semiconductor material to form a plurality of seed pads through a portion of the interface layer comprises heating at a temperature between about 500° C. and about 750° C.
 3. The method of forming a semiconductor layer of claim 1, wherein exposing the interface layer to a material comprising a semiconductor material to form a plurality of seed pads through a portion of the interface layer uses molecular beam epitaxy.
 4. The method of forming a semiconductor layer of claim 1, wherein the interface layer has a thickness of about 1 Å to about 30 Å.
 5. The method of forming a semiconductor layer of claim 1, wherein each of the plurality of seed pads has a width of about 2 nm to about 8 nm.
 6. The method of forming a semiconductor layer of claim 1, wherein the semiconductor layer comprises a threading dislocation density of about 1×10⁵ cm⁻² or less.
 7. The method of forming a semiconductor layer of claim 1, wherein the substrate comprises silicon and the plurality of seed pads comprise germanium.
 8. The method of forming a semiconductor layer of claim 1, further comprising forming a second semiconductor layer over the semiconductor layer, wherein the second semiconductor layer comprises at least one element from Group II, Group III, Group IV, Group V, and Group VI.
 9. The method of forming a semiconductor layer of claim 1, wherein the interface layer comprises at least one of, SiO₂, Si₃N₄, siliconoxynitride, and anodized aluminum oxide (AAO).
 10. The method of forming a semiconductor layer of claim 1, wherein the step of forming a semiconductor layer by lateral growth of the seed pads over the interface layer forms a semiconductor layer having a thickness greater than a critical thickness (h_(c)).
 11. A method of forming a semiconductor layer comprising: forming an oxide layer on a portion of a semiconductor substrate; forming by self-directed touchdown a plurality of seed pads comprising germanium, wherein the plurality of seed pads are interspersed within the oxide layer and contact the semiconductor substrate; and forming a germanium layer by lateral growth of the seed pads over the oxide layer.
 12. The method of forming a semiconductor layer of claim 11, wherein forming a germanium layer by lateral growth of the seed pads over the oxide layer results in the semiconductor layer comprises a threading dislocation density of less than 1×10⁵ cm⁻².
 13. The method of forming a semiconductor layer of claim 11, wherein the plurality of seed pads are separated from each other by about 1 nm to 15 nm.
 14. The method of forming a semiconductor layer of claim 11, wherein an average seed pad width is about 1 nm to 10 nm.
 15. The method of forming a semiconductor layer of claim 11, wherein the oxide layer is about 1 Å to 30 Å thick.
 16. The method of forming a semiconductor layer of claim 11, wherein the semiconductor substrate comprises silicon.
 17. The method of forming a semiconductor layer of claim 11, further comprising forming a second semiconductor layer over the semiconductor layer.
 18. The method of forming a semiconductor layer of claim 11, wherein the step of forming a germanium layer by lateral growth of the seed pads over the oxide layer forms a germanium layer having a thickness greater than 2 nm.
 19. A semiconductor device comprising: a substrate; an oxide layer disposed on a portion of the substrate; a plurality of seed pads formed by self-directed touchdown, wherein the plurality of seed pads are separated from each other by the oxide layer; and a semiconductor layer disposed over the substrate, wherein the semiconductor layer is formed by lateral growth of the seed pads over the oxide layer.
 20. The semiconductor device of claim 19, wherein the seed pad comprises germanium.
 21. The semiconductor device of claim 19, wherein the oxide is about 1 Å to 30 Å thick.
 22. The semiconductor device of claim 19, wherein the semiconductor layer comprises a threading dislocation density of less than 1×10⁵ cm⁻².
 23. The semiconductor device of claim 19, wherein the semiconductor layer has a thickness greater than a critical thickness (h_(c)).
 24. The semiconductor device of claim 19, further comprising a second semiconductor layer over the semiconductor layer. 